Ni-Fe-Cr-Mo Hastelloy X,Alloy X,UNS N06002

In the following forms:

Pipes,tubes

Buttweld Fitting

Round,Square,flat bars,rods

Plates,Sheets,Strips

Flanges & Other kinds of forgings products

 

Nickel-Iron-Chromium-Molybdenum  N06002

 

Chemical Compostion:

Material

Ni

Cr

Iron

Mn

Si     max

S    max

Mo 

P       max

W

Co 

N06002

remainder

20.5-23.5

17.0-20.0

1.00

0.05-0.15

1.00

0.030

8.0-10.0

0.04

0.20-1.0

0.5-2.5

 

Mechanical Properties:

Material

Tensile Strength,Min PSI (MPa)

Yield Strength (0.2% offset) Min(Mpa)

Elongation in 2 in. or 50mm or 4D,Min.,%

N06002

100000(690)

40000(276)

35


Standards:

Material

Seamless Tubing &/or Pipe

Welded Tubing

Welded Pipe

Buttweld fitting

Plate/Sheet/Strip

Bar Forging and Forging stock

N06002

SB-622

SB-626

SB-619

SB-366

SB-435

SB-572

 

Hastelloy X is a nickel-chromium-iron-molybdenum superalloy with outstanding high temperature strength, oxidation resistance, and
fabricability. Alloy X’s oxidation resistance is excellent up to 2200°
F. This nickel steel alloy has also been found to be exceptionally
resistant to stress-corrosion cracking in petrochemical applications.
Matrix stiffening provided by the molybdenum content results in high
strength in a solid-solution alloy having good fabrication
characteristics.  Although this nickel alloy is primarily noted for heat
and oxidation  resistance it also has good resistance to chloride
stress-corrosion cracking, carburization, and excellent resistance to
reducing or carburizing atmospheres. Two common conditions that often
lead to early failure in high temperature alloys, carburization and
nitriding, Hastelloy X resists.